Propose of design mehod for log life ultra low friction for transition metals doped DLC

• Project/Area Number: 24K00788
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 18040:Machine elements and tribology-related; Basic Section 18030:Design engineering-related; Sections That Are Subject to Joint Review: Basic Section18030:Design engineering-related , Basic Section18040:Machine elements and tribology-related
• Research Institution: Nagoya University
• Principal Investigator: 梅原 徳次 名古屋大学, 工学研究科, 教授 (70203586)
• Co-Investigator(Kenkyū-buntansha): 野老山 貴行 名古屋大学, 工学研究科, 准教授 (20432247)
• Project Period (FY): 2024-04-01 – 2027-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥18,460,000 (Direct Cost: ¥14,200,000、Indirect Cost: ¥4,260,000); Fiscal Year 2026: ¥5,460,000 (Direct Cost: ¥4,200,000、Indirect Cost: ¥1,260,000); Fiscal Year 2025: ¥5,460,000 (Direct Cost: ¥4,200,000、Indirect Cost: ¥1,260,000); Fiscal Year 2024: ¥7,540,000 (Direct Cost: ¥5,800,000、Indirect Cost: ¥1,740,000)
• Keywords: 低摩擦 / 長寿命 / トライボ反応場 / DLC / 遷移金属

Outline of Research at the Start

持続型社会では高効率化のために摩擦損失を限りなくゼロにする未来機械が求められる。超低摩擦でかつ長寿命のためには、潤滑油成分から摩擦界面を反応場として連続的に生成されるトライボケミカル反応生成物による超低摩擦の実現が考えられる。
本研究では、「トライボ反応場を模擬したオートクレーブ型摩擦装置」を試作し、種々の遷移金属を含有したカーボン系硬質膜同士において、温度と圧力と固体表面の触媒作用の摩擦界面生成物と摩擦係数に及ぼす影響を明らかにする。さらに、超低摩擦生成物の持続的生成のための必要条件を提案する。