A novel, solvent-based, high-entropy alloy that co-expresses low Young's modulus and high strength

Research Project

Project/Area Number	24K01194
Research Category	Grant-in-Aid for Scientific Research (B)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 26040:Structural materials and functional materials-related
Research Institution	University of Toyama
Principal Investigator	石本卓也富山大学, 学術研究部都市デザイン学系, 教授 (50508835)
Co-Investigator(Kenkyū-buntansha)	真中智世富山大学, 学術研究部都市デザイン学系, 特命助教 (60984606)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥18,590,000 (Direct Cost: ¥14,300,000、Indirect Cost: ¥4,290,000) Fiscal Year 2026: ¥4,810,000 (Direct Cost: ¥3,700,000、Indirect Cost: ¥1,110,000) Fiscal Year 2025: ¥6,370,000 (Direct Cost: ¥4,900,000、Indirect Cost: ¥1,470,000) Fiscal Year 2024: ¥7,410,000 (Direct Cost: ¥5,700,000、Indirect Cost: ¥1,710,000)
Keywords	生体材料 / ヤング率 / チタン合金
Outline of Research at the Start	生体にやさしい骨インプラントの創製のため、(i) 骨の萎縮と強度低下を招く応力遮蔽現象（インプラントの存在により健全な力が骨にはたらかなくなる現象）の抑制のための低ヤング率（弾性変形しやすさ）、(ii) インプラント自体の破損を防止するための高強度（永久変形しにくさ）、を併せ持つ生体用合金を得ることを目的とする。チタン合金の溶媒部分に着目することで、上記特性を同時にかつ骨生体材料として望ましい方向へと制御することを目指す。