大気腐食環境での超高強度鋼の遅れ破壊現象のモニタリングと機構解明

• Project/Area Number: 24K01204
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: National Institute for Materials Science
• Principal Investigator: 木村 勇次 国立研究開発法人物質・材料研究機構, 構造材料研究センター, 主席研究員 (80253483)
• Project Period (FY): 2024-04-01 – 2029-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥18,590,000 (Direct Cost: ¥14,300,000、Indirect Cost: ¥4,290,000); Fiscal Year 2028: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000); Fiscal Year 2027: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000); Fiscal Year 2026: ¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000); Fiscal Year 2025: ¥4,030,000 (Direct Cost: ¥3,100,000、Indirect Cost: ¥930,000); Fiscal Year 2024: ¥6,370,000 (Direct Cost: ¥4,900,000、Indirect Cost: ¥1,470,000)
• Keywords: 遅れ破壊 / 超高強度鋼 / 大気腐食 / 水素脆化

Outline of Research at the Start

引張強さが1500 MPaを超える超高強度鋼では、使用中の材料または部材がある時間経過した後に突然破断するという遅れ破壊が実用化のボトルネックとなっている。本研究は、大気腐食環境での超高強度鋼の遅れ破壊を克服するための材料設計指針構築に関する基礎的研究を行う。加工熱処理による金属組織制御によってき裂進展経路を制御した超高強度鋼材の遅れ破壊発生から最終破断までの遅れ破壊プロセスを系統的にモニタリングして、遅れ破壊挙動に及ぼす金属組織因子の影響を解明にする。これにより耐遅れ破壊特性向上に有効な金属組織因子を導き出す。