鋼材の水素侵入量可視化に基づく優れた耐水素脆化を有する新規省資源表面処理法の開発

• Project/Area Number: 24K01206
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26050:Material processing and microstructure control-related
• Research Institution: Shimane University
• Principal Investigator: 菅原 優 島根大学, 学術研究院機能強化推進学系, 教授 (40599057)
• Project Period (FY): 2024-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥18,460,000 (Direct Cost: ¥14,200,000、Indirect Cost: ¥4,260,000); Fiscal Year 2027: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000); Fiscal Year 2026: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000); Fiscal Year 2025: ¥3,510,000 (Direct Cost: ¥2,700,000、Indirect Cost: ¥810,000); Fiscal Year 2024: ¥11,310,000 (Direct Cost: ¥8,700,000、Indirect Cost: ¥2,610,000)
• Keywords: 水素侵入 / 鉄鋼材料 / 水素脆化 / 腐食 / 水素不働態化処理

Outline of Research at the Start

鉄鋼材料の水素脆化は、自動車の燃費向上や水素エネルギー社会の実現に向け非常に重要な課題である。この水素脆化の防止に向けて、これまでにエレクトロクロミック酸化物薄膜を用いて材料中への水素の侵入分布をリアルタイムで可視化する技術を開発し、腐食過程で鋼材へ侵入する水素の検出に成功した。この成果を基に本研究では、腐食環境で鋼材へ侵入する水素を定量すること、そして、鋼材の水素環境における耐環境性を高める省資源化表面処理法を開発することを目的とする。