Strategy development for achieving high strength and excellent formability in fine-grained Mg rolled sheet via deformation twinning

• Project/Area Number: 24K01213
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26050:Material processing and microstructure control-related
• Research Institution: Nagaoka University of Technology
• Principal Investigator: 中田 大貴 長岡技術科学大学, 産学融合トップランナー養成センター, 特任講師 (80800573)
• Co-Investigator(Kenkyū-buntansha): 浜 孝之 京都大学, エネルギー科学研究科, 教授 (10386633)
• Project Period (FY): 2024-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥18,590,000 (Direct Cost: ¥14,300,000、Indirect Cost: ¥4,290,000); Fiscal Year 2027: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000); Fiscal Year 2026: ¥4,810,000 (Direct Cost: ¥3,700,000、Indirect Cost: ¥1,110,000); Fiscal Year 2025: ¥3,900,000 (Direct Cost: ¥3,000,000、Indirect Cost: ¥900,000); Fiscal Year 2024: ¥6,500,000 (Direct Cost: ¥5,000,000、Indirect Cost: ¥1,500,000)
• Keywords: マグネシウム圧延材 / 微細結晶粒 / 変形双晶 / 引張特性 / プレス成形性

Outline of Research at the Start

軽量Mg合金の強度と室温成形性を同時発現させる新しい試みとして、「微細結晶粒」+「双晶」という、Mgでは相反する要素に注目した組織制御を行う。汎用元素のみからなるMg圧延材の結晶粒径および集合組織制御により、「微細結晶粒」による高強度化に加え、「双晶」による室温成形性改善を同時に達成することで、次世代の自動車パネル材として利用が進む6000系アルミニウム(Al)合金を凌駕する特性発現を成功させる。