Establishment of design guidelines for high specific strength and high conductivity aluminum alloys based on grain refinement

• Project/Area Number: 24K01214
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26050:Material processing and microstructure control-related
• Research Institution: Kanazawa University
• Principal Investigator: 宮嶋 陽司 金沢大学, 機械工学系, 准教授 (80506254)
• Co-Investigator(Kenkyū-buntansha): 足立 大樹 兵庫県立大学, 工学研究科, 教授 (00335192) ; 高田 尚記 名古屋大学, 工学研究科, 准教授 (70432523)
• Project Period (FY): 2024-04-01 – 2027-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥18,590,000 (Direct Cost: ¥14,300,000、Indirect Cost: ¥4,290,000); Fiscal Year 2026: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000); Fiscal Year 2025: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000); Fiscal Year 2024: ¥13,130,000 (Direct Cost: ¥10,100,000、Indirect Cost: ¥3,030,000)
• Keywords: 結晶粒微細化 / 導電率 / アルミニウム合金 / 遷移元素 / 熱伝導率

Outline of Research at the Start

本研究では，比較的安価な遷移元素を合金元素として有する2元系Al合金の超微細粒材を作製し，その耐熱性を解明する．その知見を基に，SPDを前提とした高比強度・高比導電率・高耐熱性を兼ね備えるモーター用Al合金の組成設計指針を確立する．比較的豊富に存在する遷移元素を用いる2元系Al合金は，実用化された場合は元素戦略の観点からも重要となる．