Characterization of Organic-Supported Porous Carbon Electrodes Prepared by Supercritical Impregnation

• Project/Area Number: 24K01243
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 27020:Chemical reaction and process system engineering-related
• Research Institution: Tohoku University
• Principal Investigator: 中安 祐太 東北大学, 学際科学フロンティア研究所, 助教 (20827042)
• Co-Investigator(Kenkyū-buntansha): 永村 直佳 国立研究開発法人物質・材料研究機構, マテリアル基盤研究センター, 主任研究員 (40708799) ; 平賀 佑也 東北大学, 工学研究科, 助教 (70757814)
• Project Period (FY): 2024-04-01 – 2027-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥18,590,000 (Direct Cost: ¥14,300,000、Indirect Cost: ¥4,290,000); Fiscal Year 2026: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000); Fiscal Year 2025: ¥5,460,000 (Direct Cost: ¥4,200,000、Indirect Cost: ¥1,260,000); Fiscal Year 2024: ¥11,180,000 (Direct Cost: ¥8,600,000、Indirect Cost: ¥2,580,000)
• Keywords: 超臨界含浸 / 有機電池 / 放射光 / 超臨界クロマトグラフィー / ポーラスカーボン

Outline of Research at the Start

超臨界二酸化炭素(scCO2)を媒体とした活性炭内への超臨界含浸法により、極性有機単分子が担持されたカーボン電極の作製を行う。その際、放射光測定を用いることで、有機単分子の活性炭表面への配向状態について明らかにする。さらに、超臨界クロマトグラフィーを用いることで、scCO2への溶解と 表面への吸着の分配比を明らかにする。それらの分析結果をフィードバックした上で、温度、圧力、含浸時間など各種条件を調整し、有機蓄電池用の電極特性の最適化を行う。