Exploration of innovative methods for the fabrication of particle-dispersed high-entropy alloys for high burn-up core materials

• Project/Area Number: 24K01393
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 31010:Nuclear engineering-related
• Research Institution: Hokkaido University
• Principal Investigator: 岡 弘 北海道大学, 工学研究院, 准教授 (10738967)
• Project Period (FY): 2024-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥18,330,000 (Direct Cost: ¥14,100,000、Indirect Cost: ¥4,230,000); Fiscal Year 2027: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000); Fiscal Year 2026: ¥5,460,000 (Direct Cost: ¥4,200,000、Indirect Cost: ¥1,260,000); Fiscal Year 2025: ¥5,980,000 (Direct Cost: ¥4,600,000、Indirect Cost: ¥1,380,000); Fiscal Year 2024: ¥4,810,000 (Direct Cost: ¥3,700,000、Indirect Cost: ¥1,110,000)
• Keywords: コールドスプレー / SMR / 酸化物分散強化 / レーザー積層造形 / 第4世代原子炉

Outline of Research at the Start

本研究では、金属積層造形法（金属3Dプリンティング）を用いて、ハイエントロピー合金中に点欠陥の消滅場所となるナノサイズ粒子を微細かつ高密度に分散した高燃焼度炉心材料用粒子分散強化型合金の直接創製に挑戦する。まず、酸化物が微細かつ均一に分散した微細組織を得るために必要な科学的因子を解明したうえで、その科学的因子を制御することにより、金属積層造形法での創製を実現する。コールドスプレー法及びレーザー積層造形法の二つの金属積層造形手法を用いる。