精良で自由度が高いキラル高分子超薄膜の創出とキラル誘起物性の探求

Research Project

Project/Area Number	24K01456
Research Category	Grant-in-Aid for Scientific Research (B)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 32020:Functional solid state chemistry-related
Research Institution	Osaka University
Principal Investigator	加藤浩之大阪大学, 大学院理学研究科, 准教授 (80300862)
Co-Investigator(Kenkyū-buntansha)	神林直哉大阪大学, 大学院理学研究科, 助教 (50706752)
Project Period (FY)	2024-04-01 – 2028-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥18,460,000 (Direct Cost: ¥14,200,000、Indirect Cost: ¥4,260,000) Fiscal Year 2027: ¥3,120,000 (Direct Cost: ¥2,400,000、Indirect Cost: ¥720,000) Fiscal Year 2026: ¥3,120,000 (Direct Cost: ¥2,400,000、Indirect Cost: ¥720,000) Fiscal Year 2025: ¥8,840,000 (Direct Cost: ¥6,800,000、Indirect Cost: ¥2,040,000) Fiscal Year 2024: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000)
Keywords	機能性らせん高分子膜 / 自己組織化単分子膜(SAM) / キラル誘起スピン選択(CISS)効果 / スピン分解光電子分光(SRPES) / 走査トンネル顕微分光法(STM/STS)
Outline of Research at the Start	本研究では、まず精良で自由度が高いキラル高分子超薄膜の製膜技術の確立を進め、様々なキラル誘起物性を研究する足掛かりを確実なものにする。そして、各種の表面分光法や顕微法を駆使して製膜した単分子膜のキャラクタリゼーションと物性評価を行い、その結果を新たな分子設計へ反映することによって高性能なキラル誘起物性の創出を目指す。キラル誘起物性の中でも、特に注目するのはキラル誘起スピン選択(CISS)効果である。CISS効果は、キラル分子膜を透過/散乱した電子のスピンが偏極する現象であるが、その理論的解釈は未だ定まっていない。本研究では、その発現機構を探ると共に、スピン選択性の向上について探求する。