Reasonable interpretation of hydrogen diffusion in metals with a new concept in consideration of a multi-trap effect

Research Project

Project/Area Number	24K07224
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 18010:Mechanics of materials and materials-related
Research Institution	Fukuoka University
Principal Investigator	山辺純一郎福岡大学, 工学部, 教授 (20532336)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,810,000 (Direct Cost: ¥3,700,000、Indirect Cost: ¥1,110,000) Fiscal Year 2026: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000) Fiscal Year 2025: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000) Fiscal Year 2024: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000)
Keywords	水素拡散 / 水素脆化 / 水素トラップ
Outline of Research at the Start	本研究では，ミクロ組織の異なる種々の実用鋼の水素拡散係数を様々な水素濃度において取得し，トラップサイトにおける水素占有率が低い条件でも水素拡散係数が水素濃度に依存する，従来手法では説明困難な実験結果を示す．さらに，実験結果を合理的に説明するため，複数のトラップサイトのトラップ水素が同時に水素拡散に関与し，水素濃度に応じてトラップ水素の寄与度が変化する新たな理論（マルチトラップ効果）を導入した独自の手法を提案する．この手法の妥当性を，網羅的な水素拡散実験と複数のトラップサイトを同時に考慮した拡散方程式の数値解析から検証する．