The evaluation of hydrogen embrittlement of weld metal with strain-induced martensite for austenite stainless steel

Research Project

Project/Area Number	24K07226
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 18010:Mechanics of materials and materials-related
Research Institution	National Institute for Materials Science
Principal Investigator	村瀬義治国立研究開発法人物質・材料研究機構, 構造材料研究センター, 主任研究員 (10354193)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000) Fiscal Year 2026: ¥390,000 (Direct Cost: ¥300,000、Indirect Cost: ¥90,000) Fiscal Year 2025: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000) Fiscal Year 2024: ¥2,470,000 (Direct Cost: ¥1,900,000、Indirect Cost: ¥570,000)
Keywords	水素脆性評価 / 汎用ステンレス鋼溶接金属 / ひずみ誘起マルテンサイト / 陰極水素チャージ / 透過水素モニタリング
Outline of Research at the Start	本研究では、安心・安全で経済自立性を有する水素供給インフラの構築に向け、汎用ステンレス鋼溶接部にひずみ誘起マルテンサイトを導入した溶接金属の水素脆性評価を行う。このため、冷間加工したSUS308溶接金属についてSKPFM（走査型ケルビンプローブ・フォース顕微鏡）によるナノ・ミクロスケール水素マッピング、EBSD（電子線後方散乱回折法）による結晶構造解析ならびにEDS（エネルギー分散型X線分光法）による元素分析を組み合わせたマルチモーダル解析を行い、水素脆性機構の検討を行うとともに、耐水素脆性に優れた汎用ステンレス鋼溶接設計技術指針を得る。