Influence of microstructure in hardened layer on fatigue crack generation for nitrocarburized steels

Research Project

Project/Area Number	24K07231
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 18010:Mechanics of materials and materials-related
Research Institution	Yokohama National University
Principal Investigator	梅澤修横浜国立大学, 大学院工学研究院, 教授 (20343171)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000) Fiscal Year 2026: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000) Fiscal Year 2025: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000) Fiscal Year 2024: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Keywords	浸窒処理 / 耐接触疲労 / 疲労き裂成長 / 転がり摩耗
Outline of Research at the Start	耐ピッチング・耐疲労強度に優れる表面硬化部材の開発が必須な状況にあるが、環境負荷低減をもたらす新規の熱処理加工プロセスにおいて、如何に表面硬化層の組織制御を行って耐き裂形成能を高めるかがその鍵を握っている。本研究では、浸窒処理に注目し、その熱処理組織の解析と組織制御による強度特性との関係を実験的に検証して明確化する。そして、疲労き裂形成過程から浸窒処理がどのように耐き裂形成に対して有効なのかを導き、浸炭焼入れや窒化を一部代替え可能な表面硬化部材の開発に寄与することを意図している。