Identification of hydrogen embrittlement-related atomic vacancies in iron and steel by in-situ positron annihilation spectroscopy

Research Project

Project/Area Number	24K08015
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 26010:Metallic material properties-related
Research Institution	Chiba University
Principal Investigator	Chiari Luca 千葉大学, 大学院工学研究院, 助教 (20794572)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000) Fiscal Year 2026: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000) Fiscal Year 2025: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000) Fiscal Year 2024: ¥2,340,000 (Direct Cost: ¥1,800,000、Indirect Cost: ¥540,000)
Keywords	水素脆化 / 空孔型欠陥 / 鉄鋼 / 陽電子消滅法 / その場測定
Outline of Research at the Start	水素インフラ用の金属材料の水素脆化機構は未解明であり，水素エネルギーの普及において喫緊の課題となっている。本研究では，水素脆化メカニズムの起因は水素誘起原子空孔の形成であることを提唱する。本研究の目的は，格子欠陥の高感度・直接プローブである陽電子消滅法の高度化によって水素脆化支配欠陥を検出することである。水素環境かつ延伸状態でのその場陽電子消滅法を開発し，水素脆化支配欠陥と思われる空孔－水素複合体の存在を立証する。新規測定法の開発で欠陥の形成からボイドの発達までの水素脆化機構を解明する。