Development of HCP-clad metals with high strength and ductility for medical devices

• Project/Area Number: 24K08019
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26010:Metallic material properties-related
• Research Institution: Kumamoto University
• Principal Investigator: 北原 弘基 熊本大学, 先進マグネシウム国際研究センター, 准教授 (50397650)
• Co-Investigator(Kenkyū-buntansha): 安藤 新二 熊本大学, 先進マグネシウム国際研究センター, 教授 (40222781)
• Project Period (FY): 2024-04-01 – 2027-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000); Fiscal Year 2026: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000); Fiscal Year 2025: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000); Fiscal Year 2024: ¥2,470,000 (Direct Cost: ¥1,900,000、Indirect Cost: ¥570,000)
• Keywords: 六方晶 / マグネシウム / 亜鉛 / チタン

Outline of Research at the Start

六方晶金属であるマグネシウムと亜鉛は生体必須元素であるため、生体吸収性材料としての応用がそれぞれ期待されている。また従来生体材料として広く利用されているチタンもまた六方晶金属である。六方晶金属は、圧延等の塑性加工により金属組織を制御することで、高い強度もしくは高い延性が得られる。しかしながら、それらの両立は困難である。本研究では、マグネシウム、亜鉛、チタンといった六方晶金属を組み合わせることで、高強度・高延性を有する生体適合性材料の開発を目的とする。