Development of Negative Thermal Expansion Materials induced by Spin State Transition utilizing Precise Control of Structural Distortion

Research Project

Project/Area Number	24K08036
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 26020:Inorganic materials and properties-related
Research Institution	Comprehensive Research Organization for Science and Society
Principal Investigator	酒井雄樹一般財団法人総合科学研究機構, 中性子科学センター, 研究員 (80758798)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000) Fiscal Year 2026: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000) Fiscal Year 2025: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000) Fiscal Year 2024: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000)
Keywords	負熱膨張 / スピン状態転移 / ペロブスカイト / 放射光 / 高圧合成
Outline of Research at the Start	ナノテクノロジーの世界では、熱膨張によるわずかな位置ズレも大きな問題となる。そこで、昇温により体積が収縮する負熱膨張材料を構造材料に混ぜることで、構造材料の熱膨張を抑制する方法が近年注目されている。本研究では、高スピンから中間スピン、または高スピンから低スピンへの温度誘起スピン状態転移という、全く新しい体積収縮メカニズムを利用した、体積収縮率10%を超えるような超巨大負熱膨張材料の開発を、構造歪みの精密制御により目指す。