Fabrication of ZnO transparent electrodes with controlled crystal planes by an aqueous solution method and their application to spectroelectrochemical sensors

Research Project

Project/Area Number	24K08042
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 26020:Inorganic materials and properties-related
Research Institution	Meiji University
Principal Investigator	我田元明治大学, 理工学部, 専任准教授 (40633722)
Co-Investigator(Kenkyū-buntansha)	岡崎琢也東京都立大学, 都市環境科学研究科, 特任准教授 (60772556)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000) Fiscal Year 2026: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000) Fiscal Year 2025: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000) Fiscal Year 2024: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000)
Keywords	酸化亜鉛 / 透明導電膜 / 水溶液法 / Chemical Bath Deposition / 分光電気化学センサー
Outline of Research at the Start	本研究では低環境負荷・低エネルギー・低コストの水溶液法により、既存の透明導電膜材料であるスズドープ酸化インジウム膜に匹敵する性能をもつ酸化亜鉛膜を作製することを目標とする。酸化亜鉛膜の脱離ガス分析と成膜条件へのフィードバックにより高性能化を目指すとともに、酸化亜鉛の結晶面制御を行い、分子の特異吸着を利用した高感度分光電気化学センサーの開発を目指す。