粉体撹拌槽を用いた両親媒性物質高含有マイクロカプセルの調製と工学的体系化

Research Project

Project/Area Number 24K08054
Research Category

Grant-in-Aid for Scientific Research (C)

Allocation TypeMulti-year Fund
Section一般
Review Section Basic Section 26030:Composite materials and interfaces-related
Research InstitutionNiigata University

Principal Investigator

田口 佳成  新潟大学, 自然科学系, 准教授 (30293202)

Project Period (FY) 2024-04-01 – 2027-03-31
Project Status Granted (Fiscal Year 2024)
Budget Amount *help
¥3,770,000 (Direct Cost: ¥2,900,000、Indirect Cost: ¥870,000)
Fiscal Year 2026: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2025: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2024: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
KeywordsMicrocapsule / Stirring / Stabilizer / Dispersion
Outline of Research at the Start

両親媒性物質などのコア物質のマイクロカプセル化では,マイクロカプセル化過程でコア物質が連続相中に漏洩し,含有率が極度に低下する。この問題を解決するために,超親水性もしくは超疎水性粉体を連続相の媒体とした粉体撹拌槽中での新規マイクロカプセル化を提案する。この方法では,まず,両親媒性のコア物質を溶解したシェル物質溶液を,撹拌している微小な粉体中に分散させることで,粉体撹拌槽中でコア物質+シェル物質溶液滴を粉体で被覆した分散性が良好なピッカリング粒子を形成する。この系を維持しながら重合を行うことでマイクロカプセルを形成する方法で,これまでにない新しい方法である。