Elucidation and control of interface structures between complex hydrides and oxide ceramics

• Project/Area Number: 24K08070
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: Hokkaido University
• Principal Investigator: 中川 祐貴 北海道大学, 工学研究院, 助教 (00787153)
• Project Period (FY): 2024-04-01 – 2027-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000); Fiscal Year 2026: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000); Fiscal Year 2025: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000); Fiscal Year 2024: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
• Keywords: 固体電解質 / リチウムイオン伝導 / 多価イオン伝導 / 錯体水素化物 / 透過電子顕微鏡

Outline of Research at the Start

リチウム系の錯体水素化物と酸化物セラミックスを複合化すると、リチウムイオン伝導度が向上することが分かっており、これは水素化物と酸化物間の界面効果によるものであると考えられている。しかし、その界面の構造は明らかになっていない。本研究では、リチウムボロハイドライド(LiBH4)と酸化物セラミックスの界面構造を電子顕微鏡を用いて解明すること、錯体水素化物と酸化物、窒化物セラミックスの界面を利用した高速多価イオン伝導材料を創製することを目的とする。