Multiscale Analysis of Ultrafine Microstructure and Mechanical properties Formed by Friction Stir Welding of High-Ni Steel

Research Project

Project/Area Number	24K08099
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 26050:Material processing and microstructure control-related
Research Institution	Osaka University
Principal Investigator	山下享介大阪大学, 接合科学研究所, 助教 (20829080)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000) Fiscal Year 2026: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000) Fiscal Year 2025: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000) Fiscal Year 2024: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
Keywords	インバー合金 / 摩擦攪拌接合 / 中性子回折 / マルチスケール解析 / マルテンサイト変態
Outline of Research at the Start	高合金オーステナイト(γ)鋼であるFe-Ni-Co系インバー合金は強度の低さ、溶接性の悪さ、低温域でのマルテンサイト(α')変態が課題であるが、微視組織制御が可能な摩擦攪拌接合(FSW)を適用できれば、上記課題の解決が期待できる。しかし、インバー合金間でγ相安定性や積層欠陥エネルギー(SFE)が異なるため、攪拌部での微視組織の形成機構は合金間で異なると予想されるが、鉄鋼材料のFSWにおいて微視組織の形成機構とSFEの関係は不明である。本研究では、マルチスケールな解析手法を駆使し、高合金γ鋼のFSWによる微視組織制御への統一的な理解と超微細粒γからのα’変態に対する新たな知見の取得を目指す。