Cutting Fabrication of Nanoparticles Dispersed Micropowders for Stereolithographic Additive Manufacturing of Ceramic Components

Research Project

Project/Area Number	24K08113
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 26050:Material processing and microstructure control-related
Research Institution	Osaka University
Principal Investigator	桐原聡秀大阪大学, 接合科学研究所, 教授 (40362587)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000) Fiscal Year 2026: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000) Fiscal Year 2025: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000) Fiscal Year 2024: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000)
Keywords	露光式造形 / 微粒子複合粉体 / セラミック部材 / 部材接合 / 立体精密計測
Outline of Research at the Start	市販の模型用光造形装置を改良し、実用セラミック部材の３Ｄプリンターとして活用する。はじめに、ナノ微粒子を複合化してマイクロ粉体とし、光硬化性樹脂へ分散してペースト化する。つぎに、ペーストをガラス容器に流し込み、底部から紫外光でパターン露光する。このとき、露光パターンを高精細にするため、複合粉体の粒度分布を最適化する。さらに、硬化物を引き上げつつ積層造形し、脱脂焼成によりセラミック部材を得る。