Prevention of fatigue fracture by controlling oxygen content and satisfactory shape of toe-of-weld part in low-temperature-transformation weld metal

Research Project

Project/Area Number	24K08115
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 26050:Material processing and microstructure control-related
Research Institution	Ehime University
Principal Investigator	水口隆愛媛大学, 理工学研究科(工学系), 准教授 (00462515)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000) Fiscal Year 2026: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000) Fiscal Year 2025: ¥3,250,000 (Direct Cost: ¥2,500,000、Indirect Cost: ¥750,000) Fiscal Year 2024: ¥520,000 (Direct Cost: ¥400,000、Indirect Cost: ¥120,000)
Keywords	溶接 / 低変態温度溶接材料 / 疲労破壊 / 表面張力
Outline of Research at the Start	変動荷重を受ける溶接構造物の破壊事故は、溶接止端部からの疲労破壊が原因であることが多い。その防止のため、溶接後の余盛形状仕上げが行われ、溶接後の工数が増加している。本申請では、低変態温度溶接材料を用いてシールドガスの組成と添加方法を変化させて溶接金属部の酸素含有量を制御と溶接金属部の溶融状態における表面張力の評価を行ったうえで、溶接ままでの余盛形状最適化による疲労破壊防止を目的とする。