Improvement in strength and stiffness of Mg-Li-Sc alloy with BCC structure by aging treatment

• Project/Area Number: 24K08122
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26050:Material processing and microstructure control-related
• Research Institution: Osaka Research Institute of Industrial Science and Technology
• Principal Investigator: 岩岡 秀明 地方独立行政法人大阪産業技術研究所, 和泉センター, 主任研究員 (90751496)
• Co-Investigator(Kenkyū-buntansha): 岩崎 真也 地方独立行政法人大阪産業技術研究所, 森之宮センター, 研究員 (00884058)
• Project Period (FY): 2024-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000); Fiscal Year 2027: ¥390,000 (Direct Cost: ¥300,000、Indirect Cost: ¥90,000); Fiscal Year 2026: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000); Fiscal Year 2025: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000); Fiscal Year 2024: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000)
• Keywords: マグネシウム合金 / 時効処理 / 強度・剛性

Outline of Research at the Start

本研究ではLiとScを添加することでBCC構造としたMg合金に対して時効処理を行い、その時の硬さやヤング率の変化を測定する。時効処理を行った試料に対して透過型電子顕微鏡や走査型電子顕微鏡による観察およびX線回折装置による分析を行い、析出物の同定やその形状および分布について評価することで析出物の形成挙動を調査する。得られた知見をもとに析出物形成が合金の強度や剛性に及ぼす影響について明らかにし、合金の高強度・高剛性化を図るための最適な合金組成や熱処理条件を確立する。