Direct observation of initial secondary inclusions nuclei in nm-order during the solidification process of iron-based alloys

Research Project

Project/Area Number	24K08125
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 26060:Metals production and resources production-related
Research Institution	The University of Tokyo
Principal Investigator	松浦宏行東京大学, 大学院工学系研究科(工学部), 准教授 (10463895)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000) Fiscal Year 2026: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000) Fiscal Year 2025: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000) Fiscal Year 2024: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Keywords	鉄鋼材料 / 非金属介在物 / 組織制御 / 核発生挙動 / 凝固プロセス
Outline of Research at the Start	介在物の分散状態を決定づける、固液界面近傍での二次介在物生成、特に凝固フロントのnmオーダー空間での初期核発生のメカニズムを解明する。上記を達成するため、本研究ではこれまでに申請者が構築してきた小型一方向凝固実験を活用する。固液界面の移動方向を制御して溶融鉄合金を凝固させた試料を用いて、nmオーダーで固液界面位置を実験的に決定する方法、発生核の検出・計測技術、固液界面－発生核の位置関係を同定する方法をそれぞれ確立したうえで、凝固フロントでの核発生位置・発生形態と発生確率、サイズ分布に及ぼす試料組成および凝固パラメーターの影響を評価して、初期核発生の機構解明を目指す。