可逆的アモルファスーアモルファス転移に伴う巨大な熱膨張現象の解明

• Project/Area Number: 24K08225
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 29010:Applied physical properties-related
• Research Institution: Muroran Institute of Technology
• Principal Investigator: 雨海 有佑 室蘭工業大学, 大学院工学研究科, 准教授 (50400065)
• Co-Investigator(Kenkyū-buntansha): 脇舎 和平 岩手大学, 理工学部, 准教授 (50781465)
• Project Period (FY): 2024-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000); Fiscal Year 2027: ¥390,000 (Direct Cost: ¥300,000、Indirect Cost: ¥90,000); Fiscal Year 2026: ¥520,000 (Direct Cost: ¥400,000、Indirect Cost: ¥120,000); Fiscal Year 2025: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000); Fiscal Year 2024: ¥2,860,000 (Direct Cost: ¥2,200,000、Indirect Cost: ¥660,000)
• Keywords: アモルファスCe合金 / アモルファスーアモルファス転移 / 巨大熱膨張 / γ-α転移

Outline of Research at the Start

本研究は，アモルファス合金の中でも最大級の熱膨張係数(55×10-6 K-1)を有するアモルファスCe-Mnにおける巨大熱膨張現象のメカニズムを解き明かすことを目的とする。室温付近で巨大な熱膨張係数が出現する温度域で電子輸送特性である電気抵抗や熱電能に履歴現象が観測された。これらの現象は，Ce単体の相転移であるγーα転移が関連した可逆的なアモルファス-アモルファス転移によるものと予測している。