Research on unusual superconducting behavior in Ir-substituted perovskite manganese oxide thin films

Research Project

Project/Area Number	24K08239
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 29020:Thin film/surface and interfacial physical properties-related
Research Institution	Tohoku University
Principal Investigator	神永健一東北大学, 工学研究科, 助教 (50831301)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000) Fiscal Year 2026: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000) Fiscal Year 2025: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000) Fiscal Year 2024: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000)
Keywords	超伝導 / 酸化物 / パルスレーザー堆積法 / PLD / LSMO
Outline of Research at the Start	銅酸化物高温超伝導体の発見後、同様な性質を持つ層状化合物が高温超伝導の候補として研究されてきた。しかし、銅酸化物以外で常圧下において100 Kを超える超伝導体はない。そうした中、最近、Ir置換ペロブスカイト型マンガン酸化物である(La,Sr)(Mn,Ir)O3薄膜において、超伝導転移温度が最大Tc = 125 Kの超伝導的挙動が観測された。本研究ではジョセフソン効果による非従来型超伝導であるか否かの検証や、Aサイト元素とIr濃度の関係の解明を通じて、本物質系の「超伝導現象」をより学術的に確固たるものにすることを目指す。