Development of crystal growth techniques to realise single-crystal thin-film halide perovskite with a large area of 10 mm

• Project/Area Number: 24K08273
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 30010:Crystal engineering-related
• Research Institution: Toin University of Yokohama
• Principal Investigator: 柴山 直之 桐蔭横浜大学, 医用工学部, 講師 (10599591)
• Co-Investigator(Kenkyū-buntansha): 中村 唯我 公益財団法人高輝度光科学研究センター, 回折・散乱推進室, テニュアトラック研究員 (90878430)
• Project Period (FY): 2024-04-01 – 2027-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000); Fiscal Year 2026: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000); Fiscal Year 2025: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000); Fiscal Year 2024: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000)
• Keywords: ペロブスカイト / 結晶 / 太陽電池

Outline of Research at the Start

溶液塗布により作製可能なハライドペロブスカイト太陽電池が注目を集めているが、エネルギー変換効率向上のためには結晶粒径の大粒径化が必要である。そこで、本研究では、エッジキャスト法による単結晶薄膜作製技術により10 mm級のハライドペロブスカイト単結晶薄膜の実現を目指す。本研究では、新規に”その場”観察X線回折測定技術を確立し、結晶化過程を可視化することで、最適な成膜条件を見出す。