Synthesis and Hierarchical Structure of Main-chain Polymer Particles Exhibiting Phase Transition by Heterogeneous Polymerization

Research Project

Project/Area Number	24K08543
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 35020:Polymer materials-related
Research Institution	Ehime University
Principal Investigator	伊藤大道愛媛大学, 理工学研究科(工学系), 講師 (40363254)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000) Fiscal Year 2026: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000) Fiscal Year 2025: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000) Fiscal Year 2024: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
Keywords	高分子構造・物性 / 高分子微粒子 / アゾベンゼン
Outline of Research at the Start	高分子微粒子は一般に真球状となる一方で、内部に結晶もしくは液晶構造をもつ場合は非真球状になる場合がある。しかし、内部構造と微粒子形状の相関については不明な点が多い。本研究ではアゾベンゼン含有高分子が構築する結晶／液晶構造とその光相転移に着目して、内部構造が崩壊する過程と微粒子形状の変化との相関から詳細を明らかにする。そのための分子設計と高分子微粒子の合成が最初の課題であり、次いで、得られた微粒子の光応答と構造物性の変化について考察する。