Development of ultra-lightweight and high-strength Mg-Li based alloys by controlling spinodal decomposition microstructure

Research Project

Project/Area Number	24K17514
Research Category	Grant-in-Aid for Early-Career Scientists
Allocation Type	Multi-year Fund
Review Section	Basic Section 26040:Structural materials and functional materials-related
Research Institution	Hirosaki University
Principal Investigator	峯田才寛弘前大学, 理工学研究科, 准教授 (20804602)
Project Period (FY)	2024-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000) Fiscal Year 2026: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000) Fiscal Year 2025: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000) Fiscal Year 2024: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
Keywords	Mg-Li合金 / 軽量合金 / 強度 / スピノーダル分解 / 組織制御
Outline of Research at the Start	肥大化する消費社会を持続的に支えるために、超軽量Mg-Li基合金の開発に注目が集まっている。しかし本合金系は強度が低く、その産業応用が広まっていない。その中で近年、特定のMg-Li基合金において熱処理によりスピノーダル分解が生じ、強度が改善することが見出された。その飛躍的な強化の要因には不明な点があり、強化メカニズムの解明とさらなる高強度化が望まれている。本研究では、スピノーダル分解制御による強度と軽量性を両立したMg-Li基合金の創製を目的とする。そのために、組織と強度の相関から強化メカニズムを解明し、その知見を基に熱処理と巨大ひずみ加工を組み合わせた組織制御による高強度化を達成する。