結晶格子欠陥を極小化させた酸化物結晶表面熱処理法の開発とその一般化

• Project/Area Number: 24K21226
• Research Category: Grant-in-Aid for Challenging Research (Pioneering)
• Allocation Type: Multi-year Fund
• Review Section: Medium-sized Section 26:Materials engineering and related fields
• Research Institution: Nagoya University
• Principal Investigator: 山本 剛久 名古屋大学, 工学研究科, 教授 (20220478)
• Project Period (FY): 2024-06-28 – 2028-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥25,610,000 (Direct Cost: ¥19,700,000、Indirect Cost: ¥5,910,000); Fiscal Year 2027: ¥4,290,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥990,000); Fiscal Year 2026: ¥6,890,000 (Direct Cost: ¥5,300,000、Indirect Cost: ¥1,590,000); Fiscal Year 2025: ¥9,100,000 (Direct Cost: ¥7,000,000、Indirect Cost: ¥2,100,000); Fiscal Year 2024: ¥5,330,000 (Direct Cost: ¥4,100,000、Indirect Cost: ¥1,230,000)
• Keywords: 結晶表面 / 透過型電子顕微鏡 / 酸化物 / 点欠陥 / 原子間力顕微鏡

Outline of Research at the Start

酸化物結晶表面を熱処理すると、結晶表面での原子拡散が促進されるだけではなく、結晶表面極近傍領域から結晶表面への排出拡散も促進される。これらの物質拡散によって、結晶最表面および表面極近傍領域の原子構造が決定される。熱処理時の温度、酸素分圧の条件を最適化することによって、表面および表面極近傍領域の原子密度を高くし、かつ、空港などの点欠陥形成を抑制した、精緻な結晶表面を構築する。そして、得られた一連の基礎データをもとに、酸化物結晶表面を熱処理するための条件を一般化させる。