| Project/Area Number |
24K22936
|
|---|
| Research Category |
Grant-in-Aid for Research Activity Start-up
|
| Allocation Type | Multi-year Fund |
|---|
| Review Section |
0301:Mechanics of materials, production engineering, design engineering, fluid engineering, thermal engineering, mechanical dynamics, robotics, aerospace engineering, marine and maritime engineering, and related fields
|
|---|
| Research Institution | Chiba Institute of Technology |
|---|
Principal Investigator |
清宮 優作 千葉工業大学, 附属研究所, 研究員 (01001586)
|
|---|
| Project Period (FY) |
2024-07-31 – 2026-03-31
|
| Project Status |
Granted (Fiscal Year 2024)
|
| Budget Amount *help |
¥2,470,000 (Direct Cost: ¥1,900,000、Indirect Cost: ¥570,000)
Fiscal Year 2025: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2024: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
|
|---|
| Keywords | 熱エネルギー貯蔵 / 潜熱蓄熱 / 二液相分離合金 / 熱物性値 / 無容器法 |
|---|
| Outline of Research at the Start |
再生可能エネルギーの普及は，持続可能な開発目標（SDGs）の達成に不可欠であり，その最大限の活用が喫緊の課題である．しかし，エネルギーの供給不安定性という問題がある．これを解決する技術として，エネルギー貯蔵材料が注目されており，二液相分離型合金は，相転移に伴う潜熱の吸・放出を利用したエネルギー密度の高い蓄熱材料として期待されている．しかし，この材料を製造する際に必要となる合金の二液相分離過程や最適な組成は不明である．本研究では，潜熱蓄熱材の開発を目指し，Fe-Cu合金の熱物性を測定して凝固組織を制御する手法を検討する．これらの結果から蓄熱材を作製し，その性能評価を行う．
|