Development of super resolved multi-material 3D printing based on thermophysical palette

• Project/Area Number: 25K01177
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 19020:Thermal engineering-related
• Research Institution: Keio University
• Principal Investigator: 田口 良広 慶應義塾大学, 理工学部(矢上), 教授 (30433741)
• Co-Investigator(Kenkyū-buntansha): 橋本 将明 慶應義塾大学, 理工学部(矢上), 助教 (00914409)
• Project Period (FY): 2025-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥18,850,000 (Direct Cost: ¥14,500,000、Indirect Cost: ¥4,350,000); Fiscal Year 2027: ¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000); Fiscal Year 2026: ¥6,630,000 (Direct Cost: ¥5,100,000、Indirect Cost: ¥1,530,000); Fiscal Year 2025: ¥7,540,000 (Direct Cost: ¥5,800,000、Indirect Cost: ¥1,740,000)
• Keywords: 熱物性 / 3D光造形 / フィラー / フェムト秒レーザー

Outline of Research at the Start

本研究の目的は、熱物性工学に基づき、異種材料によって構成されるピコリットルオーダの極微量液滴内において、フェムト秒レーザを用いた二光子吸収重合により超高精細マルチマテリアル3D光造形を達成し、例えば断熱壁と高熱輸送層が狭い空間に複雑に入り組むような全く新しいコンセプトに立脚したマイクロ熱制御デバイスを世界に先駆け実現することである。本研究により、これまで不可能であった傾斜機能材料などの複雑なマイクロ3D光造形が可能となり、革新的マイクロ熱制御デバイスの実現による新産業創出を加速する。