Understanding Degradation of Concrete Due to Carbonation of C-(A)-S-H and Inhibition Mechanism by Reactive MgO

• Project/Area Number: 25K01306
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 22010:Civil engineering material, execution and construction management-related
• Research Institution: Niigata University
• Principal Investigator: 須田 裕哉 新潟大学, 自然科学系, 准教授 (10636195)
• Project Period (FY): 2025-04-01 – 2029-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥18,850,000 (Direct Cost: ¥14,500,000、Indirect Cost: ¥4,350,000); Fiscal Year 2028: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000); Fiscal Year 2027: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000); Fiscal Year 2026: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000); Fiscal Year 2025: ¥13,910,000 (Direct Cost: ¥10,700,000、Indirect Cost: ¥3,210,000)
• Keywords: 炭酸化 / C-A-S-H / 反応性MgO / 微細ひび割れ / 炭酸化収縮

Outline of Research at the Start

混和材を多量に使用したコンクリートの中性化に関する耐久性評価において，かぶりコンクリートの中性化の評価だけでなく炭酸化後のコンクリートの品質を確保することが重要である．本研究では，混和材を多量に使用したコンクリートの中性化進行における反応性MgOの作用機構を解明する．具体的には，炭酸化が進行したカルシウムシリケート水和物の構造変化と炭酸化収縮機構の関係を明らかにする．また，反応性MgOを添加することによるMg系水和物の炭酸化機構およびC-(A)-S-Hとの相互作用，構造変化との関連を評価することで，MgO添加による新たな中性化抑制技術を構築するための基礎的知見を体系的に整理する．