Establishment of method of ultra-fine grained structure development by laminated structure

• Project/Area Number: 25K01525
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: Kanazawa University
• Principal Investigator: 古賀 紀光 金沢大学, 機械工学系, 准教授 (30735923)
• Project Period (FY): 2025-04-01 – 2029-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥18,850,000 (Direct Cost: ¥14,500,000、Indirect Cost: ¥4,350,000); Fiscal Year 2028: ¥2,340,000 (Direct Cost: ¥1,800,000、Indirect Cost: ¥540,000); Fiscal Year 2027: ¥2,600,000 (Direct Cost: ¥2,000,000、Indirect Cost: ¥600,000); Fiscal Year 2026: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000); Fiscal Year 2025: ¥12,350,000 (Direct Cost: ¥9,500,000、Indirect Cost: ¥2,850,000)
• Keywords: 積層材 / 超微細粒 / 熱膨張 / 二相鋼 / 冷却中その場観察

Outline of Research at the Start

異種金属を積層後に熱間圧延により結合させた積層材において、焼鈍後の冷却中に結晶粒径が超微細化する特異な現象が生じることが明らかとなった。従来、超微細粒形成には試料に強加工を施す必要があったが、積層材では簡便に(冷却のみで)超微細粒が得られることを意味する。本研究では、この特異な超微細粒の形成条件を明確にするとともに、その形成メカニズムを解明することで、革新的な超微細粒形成法の確立を行う。次いで、本手法の実用材料への応用として、二相鋼を用いて冷却による超微細粒形成の可否を検討する。