Study of the mechanism of damage and fracture affected by non-uniform deformation caused near grain boundaries using non-destructive observation with synchrotron radiation

• Project/Area Number: 25K01528
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: Toyohashi University of Technology
• Principal Investigator: 小林 正和 豊橋技術科学大学, 工学(系)研究科(研究院), 教授 (20378243)
• Co-Investigator(Kenkyū-buntansha): 三浦 博己 豊橋技術科学大学, 工学(系)研究科(研究院), 教授 (30219589) ; 大場 洋次郎 豊橋技術科学大学, 工学(系)研究科(研究院), 准教授 (60566793)
• Project Period (FY): 2025-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥25,740,000 (Direct Cost: ¥19,800,000、Indirect Cost: ¥5,940,000); Fiscal Year 2027: ¥5,460,000 (Direct Cost: ¥4,200,000、Indirect Cost: ¥1,260,000); Fiscal Year 2026: ¥9,620,000 (Direct Cost: ¥7,400,000、Indirect Cost: ¥2,220,000); Fiscal Year 2025: ¥10,660,000 (Direct Cost: ¥8,200,000、Indirect Cost: ¥2,460,000)
• Keywords: 結晶粒 / 局所塑性ひずみ / X線 / トモグラフィ / 金属材料

Outline of Research at the Start

局所的な微細構造とひずみの不均一な発達を理解することは，塑性変形する金属の加工硬化，熱処理（回復と再結晶を含む）および外部応力負荷下（例：割れやき裂成長）で発生する現象の理解とそれを制御し材料特性を改善するために重要である。この分野の研究を前進させるためには，塑性変形中の微細構造の発達とひずみダイナミクスの両方を包括的に特徴付ける必要がある。本研究の目標は，近年発展の著しい非破壊シンクロトロン放射技術を応用して，粒子を含むアルミニウム合金の初期結晶粒微細構造に影響を受ける局所ひずみ（特にひずみ集中）の発達に関連する直接的な証拠を得ることである。特に粒界近傍の不均一変形と損傷破壊に焦点を当てる。