Synthesis Route to Porous Ceramics via Phase Separation Induced by Thermal Conversion

• Project/Area Number: 25K01854
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 36010:Inorganic compounds and inorganic materials chemistry-related
• Research Institution: Nagoya University
• Principal Investigator: 長谷川 丈二 名古屋大学, 未来材料・システム研究所, 特任准教授 (60726412)
• Project Period (FY): 2025-04-01 – 2029-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥18,720,000 (Direct Cost: ¥14,400,000、Indirect Cost: ¥4,320,000); Fiscal Year 2028: ¥3,510,000 (Direct Cost: ¥2,700,000、Indirect Cost: ¥810,000); Fiscal Year 2027: ¥2,990,000 (Direct Cost: ¥2,300,000、Indirect Cost: ¥690,000); Fiscal Year 2026: ¥5,070,000 (Direct Cost: ¥3,900,000、Indirect Cost: ¥1,170,000); Fiscal Year 2025: ¥7,150,000 (Direct Cost: ¥5,500,000、Indirect Cost: ¥1,650,000)
• Keywords: メソポーラス材料 / 相分離 / 水熱合成 / 触媒

Outline of Research at the Start

単結晶粒子の熱分解を伴う結晶相転移に誘起される相分離を利用することで、共連続多孔構造を持つ多孔質セラミックス粒子を作製することができる。本研究では、様々な結晶系において、熱分解を伴う相転移による相分離現象を調査し、多孔質セラミックス材料の新たな作製法として広く発展させることを目的としている。加えて、この手法により作製した高比表面積セラミックス多孔体を中～高温域で使用される触媒として応用し、環境分野で社会に貢献することを目指す。