Modeling the Strength of Dual-Phase Steels Based on Quantitative Analysis of Stress Tensor and Dislocation Structure in the Hard Phase

• Project/Area Number: 25K07489
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 18010:Mechanics of materials and materials-related
• Research Institution: Tokyo City University
• Principal Investigator: 熊谷 正芳 東京都市大学, 理工学部, 教授 (20582498)
• Project Period (FY): 2025-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000); Fiscal Year 2027: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000); Fiscal Year 2026: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000); Fiscal Year 2025: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
• Keywords: 硬質相 / 応力テンソル / 転位組織 / 複相鋼 / 転位密度

Outline of Research at the Start

金属材料の強度や加工特性は、その応力状態や材料組織に大きく依存しているが、複相組織を有する金属材料の塑性変形時に硬質相に生じている応力状態や転位組織の変化、その巨視的な力学的特性への影響については、依然として明確に理解されていない。しかし、複相組織を有する高強度鋼が自動車産業などで積極的に利用される現代において、硬質相の変形や加工硬化挙動を十分理解し、材料全体の強度に与える影響を検討することは極めて重要である。この課題を解決するために、負荷を加えた供試材の回折実験を行い、各相の応力状態および転位組織を定量評価し、各相の応力ひずみ応答に基づいた巨視的な応力・ひずみ応答の強度モデルを構築する。