Study on Fatigue Fracture Mechanism of Dissimilar Joints of Steel and Aluminum Alloy by Friction Stirring

Research Project

Project/Area Number 25K07508
Research Category

Grant-in-Aid for Scientific Research (C)

Allocation TypeMulti-year Fund
Section一般
Review Section Basic Section 18010:Mechanics of materials and materials-related
Research InstitutionNational Institute of Technology, Toyama College

Principal Investigator

岡根 正樹  富山高等専門学校, その他部局等, 教授 (90262500)

Project Period (FY) 2025-04-01 – 2029-03-31
Project Status Granted (Fiscal Year 2025)
Budget Amount *help
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2028: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2027: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2026: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000)
Fiscal Year 2025: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000)
Keywords摩擦攪拌接合 / 異種金属材料接合体 / 疲労破壊
Outline of Research at the Start

申請者らは,これまで,摩擦攪拌接合(FSW)による,鉄鋼材料/Al合金異種金属接合体の疲労試験を実施し,基本的な疲労特性について明らかにしつつある。本接合材の場合,疲労破壊は,FSWによる攪拌領域内,すなわち強変形と熱影響を受けたFSW特有の複雑な組織内で発生する。したがって,疲労強度特性を明らかにするためには,その複雑な組織内で進行する疲労破壊のメカニズムを明らかにする必要がある。本研究は,新たに提案する手法を用いて,攪拌領域における変形状態を実測することで疲労破壊のメカニズムを明らかにし,より高強度で信頼性の高い異種金属接合体の創製を目指す。