Does Domain Control by Applying Strain Improve Properties of Rare-Earth-Based Superconducting Tapes?

Research Project

Project/Area Number	25K07823
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 21050:Electric and electronic materials-related
Research Institution	Kyushu Institute of Technology
Principal Investigator	岡田達典九州工業大学, 大学院工学研究院, 准教授 (50793775)
Project Period (FY)	2025-04-01 – 2028-03-31
Project Status	Granted (Fiscal Year 2025)
Budget Amount *help	¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000) Fiscal Year 2027: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000) Fiscal Year 2026: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000) Fiscal Year 2025: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
Keywords	REBCO線材 / 超伝導 / ひずみ / ドメイン制御 / 臨界電流
Outline of Research at the Start	超伝導機器の性能は臨界電流密度Jcに左右される。レアアース系超伝導体(REBCO)は優れたJc特性を示す有力材料であるが、結晶軸が入れ替わった2つのドメインが混在するという厄介な性質を持つ。我々は最近、曲げひずみ印加に伴うREBCO線材のドメイン構造変化により、超伝導特性が向上する可能性を見出した。本研究では、人工ピン（Jcを増大させる非超伝導不純物）の添加条件が異なるREBCO線材を対象に「ひずみ印加によるドメイン変化がREBCO線材の超伝導特性に与える影響」を解明する。得られた知見を基に、「ドメイン変化を利用し、超伝導機器の性能向上を図る」新たな開発指針を開拓し、超伝導技術の発展を目指す。