Nanostructure Formation Mechanisms Based on Statistical Analysis of Composition Correlograms

• Project/Area Number: 25K08254
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26010:Metallic material properties-related
• Research Institution: Nagoya University
• Principal Investigator: 齊藤 元貴 名古屋大学, 工学研究科, 助教 (00749278)
• Co-Investigator(Kenkyū-buntansha): 高田 健 大同大学, 工学部, 教授 (60373586)
• Project Period (FY): 2025-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000); Fiscal Year 2027: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000); Fiscal Year 2026: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000); Fiscal Year 2025: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000)
• Keywords: 電子顕微鏡 / 析出 / 微細組織 / 時効 / ナノ組織

Outline of Research at the Start

金属材料のマクロな特性は、内部に存在するナノメートルサイズの微細な構造（ナノ組織）に大きく影響される。本研究では、電子顕微鏡を用いて、ナノ析出物やクラスタの形や大きさ、組成の変化を詳細に観察し、さらにそれらが時間や温度によってどう変化するかを追跡する。従来困難だった微小構造の識別と定量に対して、歪みの可視化や組成分布の統計的手法を組み合わせた新しい解析法を開発し、組織変化のメカニズムを解明する。