Elucidation of the anisotropic mechanism in HDDR magnet powders based on ultramicroscopic analysis

Research Project

Project/Area Number 25K08257
Research Category

Grant-in-Aid for Scientific Research (C)

Allocation TypeMulti-year Fund
Section一般
Review Section Basic Section 26010:Metallic material properties-related
Research InstitutionKyushu University

Principal Investigator

板倉 賢  九州大学, 総合理工学研究院, 准教授 (20203078)

Co-Investigator(Kenkyū-buntansha) 赤嶺 大志  長崎大学, 総合生産科学研究科(工学系), 准教授 (40804737)
Project Period (FY) 2025-04-01 – 2028-03-31
Project Status Granted (Fiscal Year 2025)
Budget Amount *help
¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000)
Fiscal Year 2027: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2026: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2025: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
Keywordsネオジム磁石 / 結晶配向組織 / 走査透過電子顕微鏡法 / 歳差電子回折法 / 結晶方位解析
Outline of Research at the Start

水素中で熱処理するだけで高性能な異方性磁石粉末が得られる水素化・相分解・脱水素・再結合(HDDR)処理における微細粒配向メカニズムの全容解明を目指す。残留磁化(結晶配向度)が大きく異なる磁石粉末が得られるHDDR処理途中のNd-Fe-B系粉末試料を種々用意し、歳差電子回折(PED)法など走査透過電子顕微鏡(STEM)を主軸とした超顕微解析を行う。変態初期のナノ組織から従来にない高精度データを広範囲で取得して、方位マッピング像から構成相間の結晶方位関係を確定し、正方晶→立方晶→正方晶へのバリアント選択機構を解明していく。