Study on structural transfomation and mechnaical properties of fullerene solvated crystals

• Project/Area Number: 25K08281
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26020:Inorganic materials and properties-related
• Research Institution: Yokohama City University
• Principal Investigator: 橘 勝 横浜市立大学, 理学部, 教授 (80236546)
• Co-Investigator(Kenkyū-buntansha): 鈴木 凌 横浜市立大学, 理学部, 助教 (70846708)
• Project Period (FY): 2025-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000); Fiscal Year 2027: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000); Fiscal Year 2026: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000); Fiscal Year 2025: ¥2,340,000 (Direct Cost: ¥1,800,000、Indirect Cost: ¥540,000)
• Keywords: フラーレン / フラーレンウィスカー / フラーレン由来アモルファスカーボン / 弾性 / 硬さ

Outline of Research at the Start

本研究では、様々なフラーレン溶媒和結晶およびその誘導体の作製を行い、それらの力学特性をナノインデンテーション法をはじめとして種々の測定によって明らかにする。誘導体の作製には加熱処理と高圧処理を行う。微細構造の評価には、ラマン分光、X線回折、透過電子顕微鏡などを用いる。これらの結果から、構造と力学特性の相関を明らかにする。さらに、分子動力学（MD）シミュレーションを駆使して超硬カーボン材料の構造モデルを提案する。