耐照射性を有するM/HEAの不純物濃度制御による更なる高度化

• Project/Area Number: 25K08304
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: Hokkaido University
• Principal Investigator: 橋本 直幸 北海道大学, 工学研究院, 教授 (50443974)
• Project Period (FY): 2025-04-01 – 2030-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000); Fiscal Year 2029: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000); Fiscal Year 2028: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000); Fiscal Year 2027: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000); Fiscal Year 2026: ¥520,000 (Direct Cost: ¥400,000、Indirect Cost: ¥120,000); Fiscal Year 2025: ¥520,000 (Direct Cost: ¥400,000、Indirect Cost: ¥120,000)
• Keywords: 高エントロピー合金 / 侵入型不純物 / 引張強度 / 照射損傷 / 微細組織

Outline of Research at the Start

現行の原子炉及び次世代型エネルギー炉の安全な稼働には、中性子等の高エネルギー粒子照射環境に十分な耐性を持つ構造材料が必要不可欠である。これまで、構造材料として信頼性の高い各種鋼を基礎に材料開発が行われてきたが、照射損傷の遅延による耐照射性の向上及び機械的特性の維持を目指した材料開発研究は少ない。本研究では、高温境で優位な特性を示す高エントロピー合金(HEA)及び中エントロピー合金(MEA)に着目し、その機械的特性及び照射誘起2 次欠陥(フランク型転位ループ)の形成・成長挙動に及ぼす不純物（C：炭素、N：窒素、O：酸素）の役割について精査し、当該合金の高度化を図る。