Improvement of the properties of magnesium alloys with weak texture by the formation of multimodal structures

Research Project

Project/Area Number	25K08316
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 26040:Structural materials and functional materials-related
Research Institution	Toyama Prefectural University
Principal Investigator	鈴木真由美富山県立大学, 工学部, 教授 (20292245)
Project Period (FY)	2025-04-01 – 2028-03-31
Project Status	Granted (Fiscal Year 2025)
Budget Amount *help	¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000) Fiscal Year 2027: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000) Fiscal Year 2026: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000) Fiscal Year 2025: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000)
Keywords	マグネシウム合金 / 不均一組織 / 集合組織 / 力学的特性
Outline of Research at the Start	高価な希土類元素を含まず，現在次世代高速鉄道車両への応用展開も期待されており，水平マテリアルリサイクルルートの確立が急務となる難燃性Mg-Al-Ca合金を研究対象とする．対象合金に対し，室温での多軸鍛造加工で塑性加工と結晶方位制御を行い，静的熱処理を独立して行うことで加工硬化と回復・軟化を分離し，ミクロ組織の「均一度・不均一度」を制御することで強度・延性のバランスが優れたマグネシウム合金を設計する．また，ミクロ組織の均一度・不均一度が力学的特性に及ぼす影響を定量的に評価し，合金内部の組織不均一性がもたらす新たな可能性を明らかにする．