Development of Innovative Lightweight Cladding Material by Explosive Welding Method

• Project/Area Number: 25K08342
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26050:Material processing and microstructure control-related
• Research Institution: Nagoya Institute of Technology
• Principal Investigator: 成田 麻未 名古屋工業大学, 工学(系)研究科(研究院), 助教 (40886727)
• Co-Investigator(Kenkyū-buntansha): Bian Mingzhe 国立研究開発法人産業技術総合研究所, 材料・化学領域, 主任研究員 (30848320)
• Project Period (FY): 2025-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000); Fiscal Year 2027: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000); Fiscal Year 2026: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000); Fiscal Year 2025: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000)
• Keywords: 爆発圧着 / アルミニウム合金 / マグネシウム合金 / 接合界面 / 中間層

Outline of Research at the Start

本研究では，難接合材とされるマグネシウム（Mg）合金とアルミニウム（Al）に対して，接合速度が高速（約2500 m/s）であり接合界面に脆性的な中間層が形成しにくいことが特徴である「爆発圧着（爆着）法」を適用し，信頼性の高いMg/Alクラッド材を得ることを目指す。軽量材料であるMg合金の用途拡大に向け，接合界面組織を制御したAl/Mg/Al三層クラッド材を作製し，強度及び成形性に優れる革新的材料を開発する。