Control of crystal growth mode for ductility in electrodeposition using deep eutectic solvents

• Project/Area Number: 25K08347
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26050:Material processing and microstructure control-related
• Research Institution: Osaka Metropolitan University
• Principal Investigator: 瀧川 順庸 大阪公立大学, 大学院工学研究科, 教授 (70382231)
• Project Period (FY): 2025-04-01 – 2028-03-31
• Project Status: Granted (Fiscal Year 2025)
• Budget Amount: ¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000); Fiscal Year 2027: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000); Fiscal Year 2026: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000); Fiscal Year 2025: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
• Keywords: 電解析出法 / 深共晶溶媒 / 結晶成長 / 延性

Outline of Research at the Start

深共晶溶媒を用いた低温での電解析出法において、延性発現のための結晶成長モード制御法を解明し、高強度・高延性合金の作製を目的とする。具体的には、Al、Niを母相とした合金において、実験と第一原理計算とにより、電析合金の合金元素添加による結晶配向性変化と元素吸着による結合状態変化の相関を調べ、添加元素の吸着により結晶成長が阻害されない電析元素・条件を明らかにする。得られた知見から、水溶液系電析では作製不可能な、優れた機能性を発現するとともに、ミクロ欠陥フリーの材料創製による延性発現と、固溶強化、結晶粒微細化強化による高強度化を両立した、引張強度1.5 GPa、伸び10%を示す材料の創製を目指す。