Fabrication of Oxygen Evolution Reaction Electrodes using Independently Dispersed Coordination Polymer Nanocrystals for High Current Density

Research Project

Project/Area Number	25K08800
Research Category	Grant-in-Aid for Scientific Research (C)
Allocation Type	Multi-year Fund
Section	一般
Review Section	Basic Section 36020:Energy-related chemistry
Research Institution	Yamagata University
Principal Investigator	石崎学山形大学, 理学部, 准教授 (60610334)
Project Period (FY)	2025-04-01 – 2028-03-31
Project Status	Granted (Fiscal Year 2025)
Budget Amount *help	¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000) Fiscal Year 2027: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000) Fiscal Year 2026: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000) Fiscal Year 2025: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000)
Keywords	プルシアンブルー類似体 / 電気化学触媒 / 金属空気電池 / 酸素発生反応
Outline of Research at the Start	金属比制御を行った配位高分子ナノ粒子を前駆体とした高活性な酸素発生反応(OER)触媒電極の作製を目指す。触媒のナノサイズ化、凝集抑制によって触媒活性点の増加させ、高活性化を行う。このためには、ナノ触媒作製手法の開発、分散に注目した電極固定手法が必要となる。ここに申請者の独自技術である表面改質によるナノ粒子分散法を利用する。ガス拡散電極上に触媒前駆体分散液を塗布し、水酸化処理することで、高活性なOER触媒を作製する。この時に、電極表面の構造制御をナノ炭素材料（カーボンナノチューブや炭素ナノ粒子等）を用いることで進めていく。