高次組織化π共役ポリマーナノチューブ複合体のキラルπ空間制御と機能開発
Publicly Offered Research
| Project Area | Emergence of highly elaborated pai-space and its function |
|---|
| Project/Area Number |
21108522
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research on Innovative Areas (Research in a proposed research area)
|
| Allocation Type | Single-year Grants |
|---|
| Review Section |
Science and Engineering
|
|---|
| Research Institution | Kinki University |
|---|
Principal Investigator |
藤原 尚 近畿大学, 理工学部, 教授 (30190101)
|
|---|
| Project Period (FY) |
2009 – 2010
|
| Project Status |
Completed (Fiscal Year 2010)
|
| Budget Amount *help |
¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000)
Fiscal Year 2010: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
Fiscal Year 2009: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
|
|---|
| Keywords | π共役ポリマー / 高次π空間 / ナノチューブ / キラルナノ空間 / ナノ材料 |
|---|
| Research Abstract |
異種金属ナノ粒子バーコード型キラルハイブリッドナノチューブの創成を目指して、重合部位を有するキラルビスボスフィン(1)を保護基とするターチオフェンキラルホスフィン保護Au,Pdナノ粒子(1-Au NP,1-Pd NP)を合成し、ヘテロ接合バーコード型キラルナノチューブを合成した。細孔径約200nmのポーラスアルミナ膜(AM)をテンプレートとして、Auナノ粒子(1-Au NP)の電解重合(EP)により、金-ポリチオフェンハイブリッドナノチューブ修飾膜(1-Au-PT-NT-AM)を作製し、これをテンプレートに用いてPdナノ粒子(1-Pd NP)の電解重合を、次いで、アルミナ膜を水酸化ナトリウム水溶液で溶解し、バーコードナノチューブ(1-Au/Pd-PT NT)を合成し、走査型・透過型電子顕微鏡(SEM・TEM)およびエネルギー分散型X線分析(EDX)より、バーコード型ハイブリッドナノチューブ(直径約200nm)の生成を明らかにした。更に、キラル1-Au/Pd/Au-PT NTの合成にも成功した。バーコード型有機-無機ハイブリッドキラルナノチューブは初めての例である。
|