Fabrication of porous spherical ceramic particles with high laser absorption realizing high temperature circumstance and their laser powder bed fusion

Publicly Offered Research

Project Area	Creation of Materials by Super Thermal Field: Neo-3D printing by Manipulating Atomic Arrangement through Giant Potential Gradient
Project/Area Number	22H05272
Research Category	Grant-in-Aid for Transformative Research Areas (A)
Allocation Type	Single-year Grants
Review Section	Transformative Research Areas, Section (II)
Research Institution	Tohoku University
Principal Investigator	野村直之東北大学, 工学研究科, 教授 (90332519)
Project Period (FY)	2022-06-16 – 2024-03-31
Project Status	Granted (Fiscal Year 2023)
Budget Amount *help	¥8,320,000 (Direct Cost: ¥6,400,000、Indirect Cost: ¥1,920,000) Fiscal Year 2023: ¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000) Fiscal Year 2022: ¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000)
Keywords	球形多孔質セラミックス粒子 / 高レーザ吸収 / 凍結乾燥パルス圧力印加オリフィス噴射法 / 単分散粒子 / レーザ積層造形
Outline of Research at the Start	本研究では、気孔を積極的に導入した積層造形用球形セラミックス粒子を独自の手法により創製し、高レーザ吸収性と高断熱性を両立させる。90％を超える高気孔率を含有する多孔質球形セラミックス粒子を作製し積層造形を行う。粒子気孔率－レーザ吸収率－熱伝導率－セラミックス積層造形の関連を明らかにする。以上より、超温度場を利用するAM用高機能セラミックス粉末とその積層造形に関する学術基盤を創出することを目指す。