Creation of thermal field and crystallographic orientation controlling derived from metal/ceramic mixed powders

Publicly Offered Research

Project Area	Creation of Materials by Super Thermal Field: Neo-3D printing by Manipulating Atomic Arrangement through Giant Potential Gradient
Project/Area Number	24H00999
Research Category	Grant-in-Aid for Transformative Research Areas (A)
Allocation Type	Single-year Grants
Review Section	Transformative Research Areas, Section (II)
Research Institution	Kagawa University
Principal Investigator	松本洋明香川大学, 創造工学部, 教授 (40372312)
Project Period (FY)	2024-04-01 – 2026-03-31
Project Status	Granted (Fiscal Year 2025)
Budget Amount *help	¥8,320,000 (Direct Cost: ¥6,400,000、Indirect Cost: ¥1,920,000) Fiscal Year 2025: ¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000) Fiscal Year 2024: ¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000)
Keywords	レーザ粉末床溶融結合 / Al基複合材料 / 温度場 / 結晶配向 / 界面反応 / Al基セラミックス複合体
Outline of Research at the Start	金属/セラミックス(AlSi10Mg or Al /SiC) 複合体をモデル材料として, 複合粉体の異なる特性(レーザ吸収率・融点)を起点とした独自な研究アプローチに立脚し，LPBFによるAlメルト域(サブmm領域)および未溶融セラミックス界面近傍における温度場生成と結晶成長を評価・その基礎学理を深化させる。具体的には，(1)粉末粒度を調整(微細化)して界面反応を促進した緻密で多量なSiC/Al4SiC4相を含有する複合体の創製，(2) 複合粉体に由来した溶融池域および粒子間領域における温度場・凝固マップの評価とそれを基盤とした(3)α-Al，Al4SiC4相の結晶成長の基礎原理を解明する。