1991 Fiscal Year Final Research Report Summary
The CO_3^<2-> Variation of Enamel Crystals on Uptake of F^-Ion
| Project/Area Number |
02670928
|
|---|
| Research Category |
Grant-in-Aid for General Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
小児・社会系歯学
|
|---|
| Research Institution | Ohu University |
|---|
Principal Investigator |
MIYAZAWA Chyuzo Ohu University, School of Dentistry, Assistant Professor, 歯学部, 助教授 (70083441)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
IWASAKI Midori Ohu University, School of Dentistry, Assistant, 歯学部, 助手 (30168182)
|
|---|
| Project Period (FY) |
1990 – 1991
|
| Keywords | enamel / F^- ion / CO_3^<2-> ion / CO_3^<3-> radical |
|---|
| Research Abstract |
CO_3^<2-> containing about 2.0-3.7% of enamel formed stable CO_3^<3-> radical receiving irradiation of radiant ray. The fluoride solution was acted to the enamel of permanent tooth after irradiation of gamma ray. And we observed the variation of CO_3^<3-> radical associated with uptake of F^-.
As for F^- uptake of enamel, F^- concentration of fluoride solution revealed about 1000ppm at 50 and 100ppm F^-, and about 2000ppm at 500 and 1000ppm F^-. The volume of F^- uptake was increased by a high reactive concentration. However, CO_3^<2-> of enamel was decreased by about 16% at 50-100ppm F^- and 4% at 500-1000ppm.
As for ESR signal intensity of CO_3^<3-> radical of enamel using 100ppm F^-, each radical rate of 1.2% (10^4 R gamma irradiation) and 100%(10^7 R gamma irradiation)was decreased significantly compared with each one prior to an action.
CO_3^<2->/F^- of enamel revealed a secondary functional curve associated with uptake of F^-. From this reason, it was suggested that we could define the appropriate conditions in applying fluoride.
|